CO-
Polyepichlorohydrin Rubber |
Glass
Transition Temperature (°C) |
-26 |
Room
Temperature Density (°C) |
1243
<>
1383 |
Maximum
Working Temperature (°C) |
150 |
Tensile
Strength (MPa) |
M |
Resistance
To Tear |
M |
Resistance
To Abrasion |
M |
Compression
set @ -20°C (%) |
--- |
Compression
set @ +23°C (%) |
--- |
Compression
set @ +120°C (%) |
20 |
Swelling
/ 70Hr / ASTM Oil No.3 @ 150°C (%) |
5 |
Swelling
/ 70Hr / Fuel C @ Room Temperature (%) |
10 |
Gas
Permeability |
L |
Ozone
Resistance |
H |
Oxidation
Resistance |
H |
Rebound
(Hot) |
H |
Rebound
(Cold) |
H |
Heat Resistance
5 Hours (°C) |
240 |
Heat Resistance
70 Hours (°C) |
170 |
Heat Resistance
1000 Hours (°C) |
140 |
|
|