CR
- Polychloroprene Rubber |
Glass
Transition Temperature (°C) |
-45 |
Room
Temperature Density (°C) |
1233 |
Maximum
Working Temperature (°C) |
125 |
Tensile
Strength (MPa) |
H |
Resistance
To Tear |
H |
Resistance
To Abrasion |
M/H |
Compression
set @ -20°C (%) |
50 |
Compression
set @ +23°C (%) |
10 |
Compression
set @ +120°C (%) |
30 |
Swelling
/ 70Hr / ASTM Oil No.3 @ 100°C (%) |
80 |
Swelling
/ 70Hr / Fuel C @ Room Temperature (%) |
--- |
Gas
Permeability |
L |
Ozone
Resistance |
M |
Oxidation
Resistance |
VH |
Rebound
(Hot) |
VH |
Rebound
(Cold) |
VH |
Heat Resistance
5 Hours (°C) |
180 |
Heat Resistance
70 Hours (°C) |
130 |
Heat Resistance
1000 Hours (°C) |
100 |
|
|