NOTE: These values are representative values and do not relate to a specific grade of material
ECO - Epichlorohydrin Etyhlenoxide Copolymer
Glass Transition Temperature (°C) -45
Room Temperature Density (°C) 1243 <> 1383
Maximum Working Temperature (°C) 135
Tensile Strength (MPa) M
Resistance To Tear M
Resistance To Abrasion M
Compression set @ -20°C (%) ---
Compression set @ +23°C (%) ---
Compression set @ +120°C (%) 20
Swelling / 70Hr / ASTM Oil No.3 @ 150°C (%) 10
Swelling / 70Hr / Fuel C @ Room Temperature (%) 30
Gas Permeability L
Ozone Resistance H
Oxidation Resistance H
Rebound (Hot) H
Rebound (Cold) H
Heat Resistance 5 Hours (°C) 220
Heat Resistance 70 Hours (°C) 150
Heat Resistance 1000 Hours (°C) 130
This information reproduced by kind permission of SkidMark Multimedia Productions. E-REF2 is a product of SkidMark Multimedia Productions. © 1994 - 2004