NOTE:
These values are representative values and do not relate to a specific grade of material
Generic Type:
POLYCARBONATE
S.I. Abbr:
PC
Glass Transition Temperature (°C)
140
Crystalline Melting Point (°C)
N/A
Room Temperature Density (kg/m^3)
1200
Maximum Operating Temperature (°C)
115
Process Range (°C)
280 - 320
No Flow Temperature (°C)
190
Average Specific Heat Capacity (J/kg °K)
1750
Average Thermal Diffusivity (mm^2/s)
0.12
Vicat Softening Point (°C)
150
HDT (0.45 MPa) (°C)
143
HDT (1.80 MPa) (°C)
137
Chain Structure:
Amorphous
Tensile Strength (MPa)
65
Elongation @ break (%)
110
Applications
Graphical Information
Impact Strength (kJ/m)
0.700
Flexural Modulus (GPa)
2.8
Flammability Rating (UL94)
V1>V3
Drying Time (Hrs)
6
Drying Temperature (°C)
130
© SkidMark Multimedia Productions MMIV
..