Glass
Transition Temperature (°C) |
208 |
|
Crystalline
Melting Point (°C) |
240
More Info |
Room
Temperature Density (kg/m^3) |
1060 |
Maximum
Operating Temperature (°C) |
80 |
Process
Range (°C) |
250
- 300 |
No
Flow Temperature (°C) |
180 |
Average
Specific Heat Capacity (J/kg °K) |
2110 |
Average
Thermal Diffusivity (mm^2/s) |
0.09 |
Vicat
Softening Point (°C) |
135 |
HDT
(0.45 MPa) (°C) |
137 |
HDT
(1.80 MPa) (°C) |
129 |
Chain
Structure: Semi-Crystalline
|
Tensile
Strength (MPa) |
65 |
Elongation
@ break (%) |
70 |
|
Impact
Strength (kJ/m) |
0.16 |
Flexural
Modulus (GPa) |
3.00 |
Flammability
Rating (UL94) |
HB |
Drying
Time (Hrs) |
2 |
Drying
Temperature (°C) |
100 |
©