Glass
Transition Temperature (°C) |
150 |
|
Crystalline
Melting Point (°C) |
260 |
Room
Temperature Density (kg/m^3) |
1450 |
Maximum
Operating Temperature (°C) |
200 |
Process
Range (°C) |
300 - 360 |
No
Flow Temperature (°C) |
270 |
Average
Specific Heat Capacity (J/kg °K) |
1500 |
Average
Thermal Diffusivity (mm^2/s) |
0.21 |
Vicat
Softening Point (°C) |
260+ |
HDT
(0.45 MPa) (°C) |
260+ |
HDT
(1.80 MPa) (°C) |
140 |
Chain
Structure: Semi-Crystalline
|
Tensile
Strength (MPa) |
58 |
Elongation
@ break (%) |
1 |
|
Impact
Strength (kJ/m) |
0.015 |
Flexural
Modulus (GPa) |
3.76 |
Flammability
Rating (UL94) |
V0 |
Drying
Time (Hrs) |
6 |
Drying
Temperature (°C) |
150 |
©