NOTE: These values are representative values and do not relate to a specific grade of material

Generic Type: unplasticised POLY VINYL CHLORIDE S.I. Abbr: uPVC
Glass Transition Temperature (°C) 80
Crystalline Melting Point (°C) N/A
Room Temperature Density (kg/m^3) 1400
Maximum Operating Temperature (°C) 50
Process Range (°C) 160 - 210
No Flow Temperature (°C) 120
Average Specific Heat Capacity (J/kg °K) 1590
Average Thermal Diffusivity (mm^2/s) 0.08
Vicat Softening Point (°C) 80
HDT (0.45 MPa) (°C) 70
HDT (1.80 MPa) (°C) 67
Chain Structure: Amorphous
Tensile Strength (MPa) 51
Elongation @ break (%) 60
Shear Viscosity Vs Shear Rate PVT Specific Volume as a function of Pressure, Temperature Specific Heat Capacity as a function of Temperature Thermal Diffusivity as a function of Temperature
Applications
Graphical Information
Impact Strength (kJ/m) 0.080
Flexural Modulus (GPa) 3.00
Flammability Rating (UL94) V0
Drying Time (Hrs) Not Required
Drying Temperature (°C) Not Required
© SkidMark Multimedia Productions MMIV..
This information reproduced by kind permission of SkidMark Multimedia Productions. NEXUS III is a product of SkidMark Multimedia Productions. © 1994